低H2S和高CO2分压下超深井用P110SS油套管钢腐蚀特征研究 |
幸雪松1, 范白涛1, 朱新宇2, 张俊莹2, 陈长风2() |
1.中海油研究总院有限责任公司 北京 100028 2.中国石油大学(北京)新能源与材料学院 北京 102249 |
|
Corrosion Characteristics of P110SS Casing Steel for Ultra-deep Well in Artificial Formation Water with Low H2S and High CO2 Content |
XING Xuesong1, FAN Baitao1, ZHU Xinyu2, ZHANG Junying2, CHEN Changfeng2() |
1.CNOOC Research Institute Co., Ltd., Beijing 100028, China 2.School of New Energy and Materials, China University of Petroleum, Beijing 102249, China |
引用本文:
幸雪松, 范白涛, 朱新宇, 张俊莹, 陈长风. 低H2S和高CO2分压下超深井用P110SS油套管钢腐蚀特征研究[J]. 中国腐蚀与防护学报, 2023, 43(3): 611-618.
XING Xuesong,
FAN Baitao,
ZHU Xinyu,
ZHANG Junying,
CHEN Changfeng.
Corrosion Characteristics of P110SS Casing Steel for Ultra-deep Well in Artificial Formation Water with Low H2S and High CO2 Content. Journal of Chinese Society for Corrosion and protection, 2023, 43(3): 611-618.
链接本文:
https://www.jcscp.org/CN/10.11902/1005.4537.2022.225
或
https://www.jcscp.org/CN/Y2023/V43/I3/611
|
1 |
Li S L, Du J F, Guo P, et al. Suggestions on high-sulfur gasfield development [J]. Nat. Gas Ind., 2007, 27(2): 137
|
1 |
李士伦, 杜建芬, 郭 平 等. 对高含硫气田开发的几点建议 [J]. 天然气工业, 2007, 27(2): 137
|
2 |
Dai J X, Hu J Y, Jia C Z, et al. Suggestions for scientifically and safely exploring and developing high H2S gas fields [J]. Petrol. Exp. Dev., 2004, 31(2): 1
|
2 |
戴金星, 胡见义, 贾承造 等. 科学安全勘探开发高硫化氢天然气田的建议 [J]. 石油勘探与开发, 2004, 31(2): 1
|
3 |
Agrawal A K, Durr C, Koch G H. Sulfide films and corrosion rates of AISI 1018 carbon steel in saline solutions in the presence of H2S and CO2 at temperatures Up to 175F [A]. Corrosion 2004 [C]. New Orleans, 2004
|
4 |
Smith S N, Wright E J. Prediction of minimum H2S levels required for slightly sour corrosion [A]. Corrosion 1994 [C]. Houston, 1994
|
5 |
Pots B F M, Kapusta S D, John R C, et al. Improvements on de Waard-Milliams corrosion prediction and applications to corrosion management [A]. Corrosion 2002 [C]. Denver, 2002
|
6 |
Zhao G X, Wang Y C, Zhang S Q, et al. Influence mechanism of H2S/CO2-charging on corrosion of J55 steel in an artificial solution [J]. J. Chin. Soc. Corros. Prot., 2022, 42: 785
|
6 |
赵国仙, 王映超, 张思琦 等. H2S/CO2对J55钢腐蚀的影响机制 [J]. 中国腐蚀与防护学报, 2022, 42: 785
doi: 10.11902/1005.4537.2021.262
|
7 |
Zhang Q, Li Q A, Wen J B, et al. Effect of H2S partial pressure on CO2/H2S corrosion of oil tube steels [J]. Corros. Sci. Prot. Technol., 2004, 16: 395
|
7 |
张 清, 李全安, 文九巴 等. H2S分压对油管钢CO2/H2S腐蚀的影响 [J]. 腐蚀科学与防护技术, 2004, 16: 395
|
8 |
Han Y, Zhao X H, Bai Z Q, et al. Applicability of P110 steel in CO2/H2S containing environments [J]. Corros. Sci. Prot. Technol., 2012, 24: 32
|
8 |
韩 燕, 赵雪会, 白真权 等. P110钢在CO2/H2S环境中的适用性研究 [J]. 腐蚀科学与防护技术, 2012, 24: 32
|
9 |
Miao J, Bai Z Q, Yan W, et al. Corrosion factors of P110 steel in simulated CO2/H2S environment [J]. Oil Field Equip., 2004, 33(6): 53
|
9 |
苗 健, 白真权, 严 文 等. 模拟油田CO2/H2S环境P110钢的腐蚀行为研究 [J]. 石油矿场机械, 2004, 33(6): 53
|
10 |
Zhu S D, Liu H, Bai Z Q, et al. Dynamic corrosion behavior of P110 steel in stimulated oil field CO2/H2S environment [J]. Chem. Eng. Oil Gas, 2009, 38: 65
|
10 |
朱世东, 刘 会, 白真权 等. 模拟油田CO2/H2S环境中P110钢的动态腐蚀行为 [J]. 石油与天然气化工, 2009, 38: 65
|
11 |
Li D M, Long W, Zou N. Corrosion behavior of P110SS anti-sulfer pipeline steel in low H2S and high CO2 partial pressure environment of ultradeep well [J]. Surf. Technol., 2016, 45(7): 102
|
11 |
李冬梅, 龙 武, 邹 宁. 低H2S、高CO2超深井环境中P110SS抗硫钢的腐蚀行为 [J]. 表面技术, 2016, 45(7): 102
|
12 |
Choi Y S, Nesic S, Ling S. Effect of H2S on the CO2 corrosion of carbon steel in acidic solutions [J]. Electrochim. Acta, 2011, 56: 1752
doi: 10.1016/j.electacta.2010.08.049
|
13 |
Li W F, Zhou Y J, Xue Y. Corrosion behavior of 110S Tube steel in environments of high H2S and CO2 content [J]. J. Iron Steel Res. Int., 2012, 19: 59
|
14 |
Sun Q, Chen C F, Zhao X, et al. Ion-selectivity of iron sulfides and their effect on H2S corrosion [J]. Corros. Sci., 2019, 158: 108085
doi: 10.1016/j.corsci.2019.07.009
|
15 |
Yu H B, Liu J N, Yang M, et al. Effect of crystal structure and ion selectivity of corrosion products on corrosion behavior of P110S low alloy steel in H2S/CO2 environment [J]. Surf. Technol., 2020, 49(3): 28
|
15 |
于浩波, 刘家宁, 杨 明 等. 腐蚀产物晶体结构及离子选择性对P110S低合金钢在H2S/CO2环境中腐蚀行为的影响 [J]. 表面技术, 2020, 49(3): 28
|
16 |
Mao X Q, Xie J F, Fan W, et al. Corrosion behavior and material selection of tubing for a H2S containing gas well [J]. Corros. Prot., 2013, 34: 946
|
16 |
毛学强, 谢俊峰, 樊 文 等. 某气田含硫气井井筒的腐蚀行为及防腐蚀选材 [J]. 腐蚀与防护, 2013, 34: 946
|
17 |
Ma H Y, Cheng X L, Li G Q, et al. The influence of hydrogen sulfide on corrosion of iron under different conditions [J]. Corros. Sci., 2000, 42: 1669
doi: 10.1016/S0010-938X(00)00003-2
|
18 |
Goodfellow R B, Barr E. A case study of the design and operation of a high CO2 production with H2 S [A]. Corrosion 2001 [C]. Houston, Texas, 2001
|
19 |
Schutt H U, Lyle F F. CO2/H2S corrosion under wet gas pipeline conditions in the presence if bicarbonate, chloride, and oxygen [A]. Corrosion 98 [C]. San Diego, 1998
|
20 |
Kvarekval J, Nyborg R, Seiersten M. Corrosion product films on carbon steel in semi-sour CO2/H2S environments [A]. Corrosion 2002 [C]. Denver, 2002
|
21 |
Zhao G X, Lv X H, Li H L, et al. Effect of temperature on CO2 corrosion behaviour of P110 steel [J]. J. Chin. Soc. Corros. Prot., 2005, 25: 93
|
21 |
赵国仙, 吕祥鸿, 李鹤林 等. 温度对P110钢CO2腐蚀行为的影响 [J]. 中国腐蚀与防护学报, 2005, 25: 93
|
22 |
Zhu S D, Yin Z F, Bai Z Q, et al. Influences of temperature on corrosion behavior of P110 steel [J]. J. Chin. Soc. Corros. Prot., 2009, 29: 493
|
22 |
朱世东, 尹志福, 白真权 等. 温度对P110钢腐蚀行为的影响 [J]. 中国腐蚀与防护学报, 2009, 29: 493
|
23 |
Bai H T, Yang M, Dong X W, et al. Research progress on CO2 corrosion product scales of carbon steels [J]. J. Chin. Soc. Corros. Prot., 2020, 40: 295
|
23 |
白海涛, 杨 敏, 董小卫 等. CO2腐蚀产物膜的研究进展 [J]. 中国腐蚀与防护学报, 2020, 40: 295
doi: 10.11902/1005.4537.2019.150
|
24 |
Li J, Lu M X, Yan M L, et al. Corrosion mechanism of steel P110 in CO2-containing simulated oilfield brine [J]. J. Chin. Soc. Corros. Prot., 1999, 19: 285
|
24 |
李 静, 路民旭, 严密林 等. 模拟油田水介质中P110钢的CO2腐蚀机理 [J]. 中国腐蚀与防护学报, 1999, 19: 285
|
25 |
Ming N X, Wang Q S, He C, et al. Effect of temperature on corrosion behavior of X70 steel in an artificial CO2-containing formation water [J]. J. Chin. Soc. Corros. Prot., 2021, 41: 233
|
25 |
明男希, 王岐山, 何 川 等. 温度对X70钢在含CO2地层水中腐蚀行为影响 [J]. 中国腐蚀与防护学报, 2021, 41: 233
doi: 10.11902/1005.4537.2020.049
|
26 |
He S, Wang B, Xie R J, et al. Corrosion behavior of 110SS steel in supercritical CO2 phase under environment with low H2S [J]. Equip. Environ. Eng., 2021, 18(1): 64
|
26 |
何 松, 王 贝, 谢仁军 等. 低含H2S工况下110SS的超临界CO2腐蚀行为 [J]. 装备环境工程, 2021, 18(1): 64
|
27 |
Zhang L, Yang J, Sun J, et al. Effect of pressure on wet H2S/CO2 corrosion of pipeline steel [A]. Corrosion 2009 [C]. Onepetro, 2009
|
28 |
Kvarekval J, Nyborg R, Choi H. Formation of multilayer iron sulfide films during high temperature CO2/H2S corrosion of carbon steel [A]. Corrosion 2003 [C]. San Diego, 2003
|
29 |
Shi F X, Lei Z, Yang J W, et al. Polymorphous FeS corrosion products of pipeline steel under highly sour conditions [J]. Corros. Sci., 2016, 102: 103
doi: 10.1016/j.corsci.2015.09.024
|
30 |
Lv X H, Zhao G X, Zhang J B, et al. Corrosion behaviors of super 13Cr martensitic stainless steel under CO2 and H2S/CO2 environment [J]. J. Univ. Sci. Technol. Beijing, 2010, 32: 207
|
30 |
吕祥鸿, 赵国仙, 张建兵 等. 超级13Cr马氏体不锈钢在CO2及H2S/CO2环境中的腐蚀行为 [J]. 北京科技大学学报, 2010, 32: 207
|
31 |
He X L, Zhao G X, Liu H. Corrosion behavior of 3Cr and P110 steel in simulated environment containing CO2/H2S [J]. Welded Pipe Tube, 2009, 32(3): 15
|
31 |
何兴利, 赵国仙, 刘 会. 模拟油田CO2/H2S环境下3Cr和P110钢的腐蚀行为研究 [J]. 焊管, 2009, 32(3): 15
|
32 |
Crolet J L, Thevenot N, Dugstad A. Role of free acetic acid on the CO2 corrosion of steels [A]. Corrosion 99 [C]. San Antonio, 1999
|
33 |
Li J L, Ma H X, Zhu S D, et al. Erosion resistance of CO2 corrosion scales formed on API P110 carbon steel [J]. Corros. Sci., 2014, 86: 101
doi: 10.1016/j.corsci.2014.04.051
|
34 |
Loukachenko N, Bourges P, Orie K E, et al. Recent experience on sour service resistant steels behavior [A]. Corrosion 2009 [C]. Atlanta, 2009
|
35 |
LI X D, Qi Y M, Chen C F, et al. Investigation of mechanical property of oil tube steel P110S in high temperature and high pressure environment containing H2S/CO2 [J] J. Iron Steel Res. Int., 2011, 18: 685
|
36 |
Sardisco J B, Pitts R E. Corrosion of iron in an H2S-CO2-H2O system mechanism of sulfide film formation and kinetics of corrosion reaction [J]. Corrosion, 1965, 21: 245
doi: 10.5006/0010-9312-21.8.245
|
37 |
Asadian M, Sabzi M, Anijdan S H M. The effect of temperature, CO2, H2S gases and the resultant iron carbonate and iron sulfide compounds on the sour corrosion behaviour of ASTM A-106 steel for pipeline transportation [J]. Int. J. Pressure Vessels Pip., 2019, 171: 184
doi: 10.1016/j.ijpvp.2019.02.019
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|